Description:
This is a one component gun grade polyurethane based construction sealant, it is of low modulus and cures by reaction with atmospheric moisture to form a soft rubber like material with excellent elastic and adhesion strength.
Applications:
Features:
Technical Data:
| Item | Range | Typical Data | Typical Data | Typical Data | 
| Appearance | Black/White/Grey Homogenous paste | Black Homogenous paste | White Homogenous paste | Grey Homogenous paste | 
| Extrudability (ml/min)GB/T13477.4 | ≥80 | 105 | 100 | 100 | 
| Sagging Properties (mm) GB/T13477.6 | 0 | 0 | 0 | 0 | 
| Tack free time (min) GB/T 13477.5 | 1~3 | 2 | 2 | 2 | 
| Volatile content (%) GB/T13477.19 | ≤4 | 3 | 3 | 3 | 
| Shore A – hardness GB/T 531.1 | 25~35 | 28 | 28 | 28 | 
| Tensile strength (Mpa) GB/T 528 | ≥0.8 | 1.0 | 1.0 | 1.0 | 
| Elongation at break (%) GB/T 528 | ≥600 | 700 | 700 | 700 | 
| Tensile modulus (Mpa) GB/T13477.8 23ºC / -20ºC | ≤0.4(60%) / ≤0.6 (60%) | 0.30 / 0.50 | 0.30 / 0.50 | 0.30 / 0.50 | 
| Tensile properties at maintained extension GB/T13477.10 | No failure | No failure | No failure | No failure | 
| Adhesion/cohesion properties at maintained extension after water immersion GB/T13477.11 | No failure | No failure | No failure | No failure | 
| Adhesion/cohesion properties at variable temperature GB/T13477.13 | No failure | No failure | No failure | No failure | 
| Elastic recovery rate (%) GB/T13477.10 | ≥70 | 80 | 80 | 80 | 
| Operating Temperature (ºC): | -40~90 | |||
Note: All data above were tested under standardized condition
Regular Colors: Black,White, Grey
Packing:
310ml cartridge * 20 or 12pcs/carton
600ml sausage * 20pcs/carton
Shelf Life: 9 months in dry and cool place
|   | 
 
                                 
                                 
                                 
                                